AKROTEK®

PK-VM ICF 15 black (6074)PK CF15

AKROTEK® PK-VM ICF 15 black (6074) is a 15% carbon fibre reinforced polyketon with good sliding properties.

Features

hydrolysis / chemically stabilised

Properties

Modulus

9.000MPa

Strength

90MPa

Impact

30kJ/m²

Sustainability


Recycled content

15 %

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9000 MPa
8800 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
90 MPa
90 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
1,5 %
1,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8600 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
120 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30 kJ/m²
30 kJ/m²

Thermal Properties


Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

General properties


Density

ISO 1183

23°C
1,26 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,7 - 0,8 %

Molding shrinkage

ISO 294-4

flow
transverse
0,4 - 0,6 %
1,0 - 1,2 %

Electrical Properties


Surface resistivity

DIN EN 62631-3-2

d.a.m.
104

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.