AKROMID®
AKROMID® T9 GF 50 natural (8334) is a 50% glass fibre reinforced polyphthalamide with heat stabilization, high rigidity and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
Properties
16.500MPa
250MPa
95kJ/m²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 179-1/1eU
ISO 179-1/1eA
ISO 11357-2
ISO 11357-3
UL 94
ISO 1183
Discover all the technical specifications at a single glance here.
The values mentioned are recommendations. We only recommend desiccant / dry air dryers or vacuum dryers. Too long a drying time and the resulting residual moisture content below the lower limit can lead to filling problems and surface defects. The specified drying time refers to closed and undamaged bagged material. When processing from previously opened bags or from octabins with polyolefin inliners, a longer drying time may be necessary. It is recommended to check the residual moisture content after the drying process.
Drying time
0 - 4 h
Drying temperature (τ ≤ -30°C)
120 °C
Processing moisture
0,02 - 0,1 %
Feed section
60 - 90 °C
Temperature Zone 1 - Zone 4
300 - 340 °C
Nozzle temperature
310 - 350 °C
Melt temperature
310 - 340 °C
Mold temperature
120 - 160 °C
Holding pressure, spec.
300 - 800 bar
Back pressure, spec.
50 - 150 bar
Injection speed
medium to high
Screw speed
8 - 15 m/min
Explore more exciting application examples that illustrate how our products can be beneficial to you in various situations and industries.
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.