AKROMID®

Preliminary

T9 GF 30 grey (8134)PPA GF30

AKROMID® T9 GF 30 grey (8134) is a 30% glass fiber reinforced polyphthalamide colored in grey, similar to RAL 7047. Not only is it characterised by very high stiffness and strength, but also by its high temperature and chemical resistance. Based on PA9T, the material has a lower moisture absorption and a Tg which is more constant compared to conventional PA6T variants. Therefore, it is perfectly suitable for parts with tight dimensional tolerances which are exposed to high mechanical loads.

Features

heat stabilised 160
hydrolysis / chemically stabilised
E&E
reduced moisture

Properties

Modulus

10.000MPa

Strength

190MPa

Impact

70kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
10000 MPa
9500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
190 MPa
160 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,8 %
2,1 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
70 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
10 kJ/m²

Thermal Properties


Melting temperature

ISO 11357-3

DSC, 10K/min
305 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
155 °C
125 °C

Flammability


Burning rate

UL 94

1,6 mm Wall thickness
HB Class

General properties


Density

ISO 1183

23°C
1,38 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,6 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.