AKROMID®

Preliminary

NEXT B28 GF 30 9 FR black (8342BMBCI)PA6 GF30 FR(40)

AKROMID® NEXT B28 GF 30 9 FR black (8342BMBCI) is a flame retardant PA6 with 30% glass fibres. The flame retardant system is free of red phosphorus and halogens, leading to optimised electrical properties for e-mobility applications. This grade meets the riquirement according UL94 V0@1.6mm. Due to its very good flowability, it is characterised by easy processability as well as good surface properties. The material has excellent long-term thermal stability and outstanding mechanical properties. The compound is certified according to ISCC PLUS. It includes sustainable biomass-balanced raw materials (PA6 and flame retardant).

Features

biomass balanced
heat stabilised 130
electrically neutral
E-Mobility
E&E
easy flow

Properties

Modulus

10.200MPa

Strength

148MPa

Impact

75kJ/m²

Sustainability


Allocation factor

only valid for ISCC PLUS/REDcert² certified products

94 %

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
10200 MPa
7000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
148 MPa
98 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,2 %
4,6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
75 kJ/m²
80 kJ/m²

Thermal Properties


Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
207 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
165 °C
135 °C

Flammability


Burning rate

UL 94

1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
960 °C

HWI

UL 746A

1,6 mm Wall thickness
3,2 mm Wall thickness
0 PLC
0 PLC

HAI

UL 746A

1,6 mm Wall thickness
3,2 mm Wall thickness
0 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties


Density

ISO 1183

23°C
1,37 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,0 - 2,2 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,6 - 0,8 %

Electrical Properties


Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1010 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1012

Comparative tracking index

IEC 60112

Test liquid A
600 V

Comparative tracking index

ASTM D3638

0 PLC

Dielectric strength

IEC 60243

3 mm
18 kV/mm

Inclined-Plane Tracking, IPT

ASTM D2303-13

1,5 kV

High voltage arc tracking rate (HVTR)

UL 746A

1 PLC

High Volt, Low Current Arc Resistance

ASTM D495

4 PLC

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.