AKROMID®

UL

C3 GF 30 1 FR black (7243)PA66+PA6 GF30 FR(40)

AKROMID® C3 GF 30 1 FR black (7243) is a 30 % glass fiber reinforced, flame retardant and heat stabilised PA6/6.6 blend. Listed to UL 94 in all-colours, the material is based on a flame retardant system that is free of red phosphorus and halogens. Due to its good flowability, an improved surface quality is achieved. This grade is also suitable E&E applications (e.g. control cabinets) as well as for railroad applications and meets the requirements for public transportation (EN 45545-2 R22/23/24/26 HL3).

Features

heat stabilised 130
electrically neutral
flame retardant
E&E
public transportation
easy flow

Regulatory

en45545-2ul

Properties

Modulus

10.800MPa

Strength

148MPa

Impact

74kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
10800 MPa
7500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
148 MPa
105 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,0 %
5,3 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
74 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
9 kJ/m²

Thermal Properties


Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
225 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
251 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
168 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Ball pressure test

IEC 60695-10-2

> 210 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
155 °C
130 °C

Flammability


Burning rate

UL 94

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class
V-0 Class

Burning rate 5V

UL 94

1,6 mm Wall thickness
3,2 mm Wall thickness
5VA Class
5VA Class

GWFI

IEC 60695-2-12

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
960 °C
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
725 °C
725 °C
725 °C
775 °C

HWI

UL 746A

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC
0 PLC

HAI

UL 746A

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

Protection Train

EN 45545-2

R22/R23/R24/R26 HL3

General properties


Density

ISO 1183

23°C
1,42 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,6 - 1,8 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,6 - 0,8 %

Electrical Properties


Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1012 Ω x cm

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Comparative tracking index

ASTM D3638

UL
0 PLC

Dielectric strength

IEC 60243

UL
3 mm
24,6 kV/mm

Inclined-Plane Tracking, IPT

ASTM D2303-13

UL
1 kV

High voltage arc tracking rate (HVTR)

UL 746A

UL
0 PLC

High Volt, Low Current Arc Resistance

ASTM D495

UL
6 PLC

Rheological Properties


Flowability

AKRO

2 mm Thickness
460 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.