AKROMID®

B3 9 natural (6409)PA6

AKROMID® B3 9 natural (6409) is an unreinforced polyamide 6 with good flowability and very good demoulding properties. It is suitable for applications in the furniture industry, the sport and leisure as well as the automotive industry. The material has a light inherent color.

Features

Sports & leisure

Properties

Modulus

3.300MPa

Strength

85MPa

Impact

Na

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
3300 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
85 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.
4 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
17 %

Thermal Properties


Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
60 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
180 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability


Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties


Density

ISO 1183

23°C
1,13 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
1,0 - 1,2 %
1,1 - 1,3 %

Electrical Properties


Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1013 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1012

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.