AKROMID®

UL
Preliminary

B3 1 FR grey (8397)

PA 6 FR (30)

AKROMID® B3 1 FR grey (8397) is an unreinforced, flame retardant and heat stabilised PA6 colored in light grey (similar to RAL 7035). Listed to UL 94 in all-colours, the material is based on a flame retardant system that is free of red phosphorus and halogens.

Features

heat stabilised 130
flame retardant
easy flow
E&E
public transportation

Regulatory

ul

Properties

Modulus

3.600MPa

Strength

72MPa

Impact

Na

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
3600 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
72 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
> 5 %

Thermal Properties


UL

RTI electrical

UL 746B

0,4mm Wall thickness
0,8mm Wall thickness
1,6mm Wall thickness
3,2mm Wall thickness
65 °C
65 °C
65 °C
65 °C

UL

RTI impact

UL 746B

0,4mm Wall thickness
0,8mm Wall thickness
1,6mm Wall thickness
3,2mm Wall thickness
65 °C
65 °C
65 °C
65 °C

UL

RTI strength

UL 746B

0,4mm Wall thickness
0,8mm Wall thickness
1,6mm Wall thickness
3,2mm Wall thickness
65 °C
65 °C
65 °C
65 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability


UL

Burning rate

UL 94

0,4mm Wall thickness
0,8mm Wall thickness
1,6mm Wall thickness
3,2mm Wall thickness
V-0 Class
V-0 Class
V-0 Class
V-0 Class

UL

HWI

UL 746A

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
4 PLC
4 PLC
0 PLC
0 PLC

UL

HAI

UL 746A

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties


Density

ISO 1183

23°C
1,19 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,9 - 1,1 %
1,0 - 1,2 %

Electrical Properties


Comparative tracking index

IEC 60112

Test liquid A
600 V

Dielectric strength

IEC 60243

3 mm
10 kV/mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.